Simpson Strong-Tie SET-3G56 High-Strength Epoxy Adhesive - 56oz Tube
SET-3G is the latest innovation in epoxy anchoring adhesives with high design strength and proven performance. SET-3G is a 1:1 ratio, two-component, anchoring adhesive for concrete (cracked and uncracked). SET-3G installs and performs in a variety of environmental conditions and temperature extremes.
Key Features
- Exceptional performance — superior bond strengths permit ductile solutions in high seismic areas
- Design flexibility — improved sustained load performance at elevated temperature
- Jobsite versatility — can be specified for all base material conditions when in-service temperatures range from -40°F (-40°C) to 176°F (80°C)
- Recognized per ICC ES AC308 for post-installed rebar development and splice length design provisions
- Code listed for installation with the Speed Cleanâ„¢ DXS, dustless drilling system without further hole cleaning
- Wire brush hole-cleaning system for conventional blow-brush-blow cleaning method for anchoring
- With higher bond strengths, ductile solutions can often be achieved with SET-3G in high seismic areas
- Low-odor formulation
- Manufactured in the USA using global materials
- During the installation of SET-3G, when the correct installation processes are followed, there is no performance difference between water-saturated concrete, water-filled holes, or submerged concrete
- For use with potable water
Specifications:
| Mix Ratio/Type | 1:1 epoxy |
| Mixed Color | Gray |
| Base Materials | Concrete — cracked and uncracked |
| Base Material Conditions | Dry, water-saturated, water-filled and submerged |
| Anchor Type | Threaded rod or rebar |
| Substrate Installation Temperature | 40°F (4°C) to 100°F (38°C) |
| In-Service Temperature Range | -40°F (-40°C) to 176°F (80°C) |
| Storage Temperature | 45°F (7°C) and 90°F (32°C) |
| Shelf Life | 24 months |
| Volatile Organic Compound (VOC) | 2 g/L |
Applications
- Mass Timber / Cross-Laminated Timber
- Seismic (New Construction)
- Water / Wastewater Facilities
- Concrete: Cracked
- Seismic Retrofit
Included Parts
- EMN22i - One mixing nozzle and extension included with SET3G10 and SET3G22-N
Specifications:
| Model No. | Option | Packaging Qty. | Carton Qty. | Compatible Tools |
|---|
| SET3G10 | 8.5-oz. coaxial cartridge | 1 | 12 | CDT10S dispensing tool / EMN22i mixing nozzle (included) |
| SET3G22-N | 22-oz. side-by-side cartridge | 1 | 10 | EDT22S, EDTA22P, EDTA22CKT dispensing tools / EMN22i mixing nozzle (included) |
| SET3G56 | 56 oz. side-by-side cartridge | 1 | 6 | EDTA56P dispensing tool / EMN22i mixing nozzle (not included) |
Applications
- Threaded rod anchor and rebar dowel installations in cracked and uncracked concrete under a wide variety of environmental installation and use conditions
- Installation in downward, horizontal and upwardly inclined (including overhead) orientations
- Qualified for use in structures assigned to Seismic Design Categories A through F
Installation
- Surfaces to receive epoxy must be clean per approved hole cleaning method.
- Base-material temperatures must be 40°F (4°C) or above at the time of installation. For best results, adhesive should be conditioned to a temperature between 70°F (21°C) and 80°F (37°C) at the time of installation.
- To warm cold adhesive, store cartridges in a warm, uniformly heated area or storage container. Do not immerse cartridges in water or use microwave to facilitate warming.
- Mixed material can harden in the dispensing nozzle within 30 minutes at 70°F (21°C).
- Use only Simpson Strong-Tie mixing nozzles in accordance with Simpson Strong-Tie instructions. Modification or improper use of mixing nozzle may impair SET-3G adhesive performance.
- For full instructions, see Adhesive Anchoring Installation Instructions.
Test Criteria
- SET-3G has been tested in accordance with ICC-ES AC308, ACI 355.4 and applicable ASTM test methods.
Cure Schedule
Specifications:
Concrete
Temperature °F | Concrete
Temperature °C | Gel Time (mins.) | Cure Time (hrs.) |
1. For SI: 1°F = (°C x 9/5) + 32.
2. For water-saturated concrete, water-filled holes and submerged concrete, the cure times should be doubled.
3. For installation of anchors in concrete where the temperature is below 70°F (21°C), the adhesive must be conditioned to a minimum temperature of 70°F (21°C). |
| 40 | 4 | 120 | 192 |
| 50 | 10 | 75 | 72 |
| 60 | 16 | 50 | 48 |
| 70 | 21 | 35 | 24 |
| 90 | 32 | 25 | 24 |
| 100 | 38 | 15 | 24 |
SET-3G Typical Properties
Specifications:
| Property | Class B | Class C | Test Method |
| (40°–60°F) | (>60°F) |
| Consistency | Non-sag | Non-sag | ASTM C881 |
| Bond Strength, Slant Shear | Hardened to Hardened Concrete, 2-Day Cure1 | 3,700 psi | 3,300 psi | ASTM C882 |
| Hardened to Hardened Concrete, 14-Day Cure1 | 3,850 psi | 3,350 psi |
| Fresh to Hardened Concrete, 14-Day Cure2 | 2,750 psi | 2,750 psi |
| Compressive Yield Strength, 7-Day Cure2 | 13,000 psi | 15,350 psi | ASTM D695 |
| Compressive Modulus, 7-Day Cure2 | 650,000 psi | 992,000 psi | ASTM D695 |
| Heat Deflection Temperature, 7-Day Cure2 | 147°F (64°C) | ASTM D648 |
| Glass Transition Temperature, 7-Day Cure2 | 149°F (65°C) | ASTM E1356 |
| Decomposition Temperature, 24-Hour Cure2 | 500°F (260°C) | ASTM E2550 |
| Water Absorption, 24-Hours, 7-Day Cure2 | 0.13% | ASTM D570 |
| Shore D Hardness, 24-Hour Cure2 | 84 | ASTM D2240 |
| Linear Coefficient of Shrinkage, 7-Day Cure2 | 0.002 in./in. | ASTM D2566 |
| Coefficient of Thermal Expansion2 | 2.3 x 10-5 in./in.°F | ASTM C531 |
- Material and curing conditions: Class B at 40° ± 2°F, Class C at 60° ± 2°F.
- Material and curing conditions: 73° ± 2°F.
|